| Property | Test temp | Unit | Requirements | CYCT Value | Test Method | |
| Thickness | - | mm | ≥Specified minimum value | 1.8 | Annex B | |
| Glass transition temperature | - | °C | At least 20°C below minimum application temperature | ≤-56℃ | ISO 11357-2 | |
| Crystallization temperature | - | °C | No evidence of crystallization | No evidence of crystallization | ISO 11357-3 | |
| Holiday detection at 5 kV/mm + 5 kV, max. 25 kV | - | -- | no holiday | no holiday | Annex C | |
| Drip Resistance | Tmax+20°C (Minimum 80°C) | -- | No Dropping of compound | No Dropping of compound | Annex K | |
| Adhesion test of reinforced compound with respect to steel and to plant coating | 23°C | N/mm | ≥0.04 / Cohesive separation mode Coverage ≥ 95% | 0.40 / Cohesive separation mode Coverage >95% | Annex H (and M.3 and Annex I) | |
| 95°C | ≥0.02 / Cohesive separation mode Coverage ≥ 95% | 0.03 / Cohesive separation mode Coverage >95% | ||||
| Adhesion test of reinforced compound with respect to steel and to plant coating after thermal ageing, for 100 days at Tmax + 20°C | 23°C | N/mm | ≥0.04 / Cohesive separation mode Coverage ≥ 95% | 0.38 / Cohesive separation mode Coverage >95% | Annex H (and M.3 and Annex I) | |
| 95°C | ≥0.02 / Cohesive separation mode Coverage ≥ 95% | 0.04 / Cohesive separation mode Coverage >95% | ||||
| Adhesion test of reinforced compound with respect to steel and to plant coating after hot-water immersion, for 100 days at Tmax + 20°C | 23°C | N/mm | ≥0.04 / Cohesive separation mode Coverage ≥ 95% | 0.35 / Cohesive separation mode Coverage >95% | Annex H (and M.3 and Annex I) | |
| 95°C | ≥0.02 / Cohesive separation mode Coverage ≥ 95% | 0.025 / Cohesive separation mode Coverage >95% | ||||
| Adhesion test of compound without reinforcement with respect to steel and to plant coating before and after thermal ageing and before and after hot-water immersion, both for 100 days at Tmax + 20°C | 23°C | - | The coating shall leave a film of compound on the substrate. | The coating leave a film of compound on the substrate. | 13.5.9 (and M.3 and Annex I) | |
| 95°C | ||||||
| Lap shear resistance | 23°C | N/mm² | ≥0.004 / Cohesive separation mode Coverage ≥95% | 0.025 / Cohesive separation mode Coverage ≥95% | Annex I | |
| 95°C | ≥0.002 / Cohesive separation mode Coverage ≥95% | 0.003 / Cohesive separation mode Coverage ≥95% | ||||
| Specific electrical insulation resistance | RS100 | 23°C | Ω·m² | ≥108 / ≥0.8a | 1.0x1010 / 0.9 | Annex F |
| RS100/RS70 | - | |||||
| Complete Coating | ||||||
| Impact resistance | 23°C | J | ≥15 | >15 | Annex D | |
| Indentation resistance | FJC Type | 23°C and 95°C | N/mm² | 13A | 13A | Annex E |
| Test pressure | 1.0 | 1.0 | ||||
| Residual thickness | mm | ≥0.6 | 1.2 | |||
| Cathodic disbondment resistance at 28 days | 23°C and 95°C | mm | 0 mm, no holiday | 0 mm, no holiday | Annex G (and Annex C and 13.5.7) | |