Property

Test Temp

Unit

Requirements

Value

Test Method

Thickness

-

mm

≥Specified minimum value

1.8

Annex B

Glass transition temperature

-

°C

At least 20°C below minimum application temperature

≤-56℃

ISO 11357-2

Crystallization temperature

-

°C

No evidence of crystallization

No evidence of crystallization

ISO 11357-3

Holiday detection at 5 kV/mm + 5 kV, max. 25 kV

-

--

no holiday

no holiday

Annex C

Drip Resistance

Tmax+20°C (Minimum 80°C)

--

No Dropping of compound

No Dropping of compound

Annex K

Adhesion test of reinforced compound with respect to steel and to plant coating

23°C

N/mm

≥0.04

Cohesive separation mode Coverage ≥ 95%

0.40

Cohesive separation mode Coverage ＞95%

Annex H (and M.3 and Annex I)

95°C

≥0.02

0.03

Adhesion test of reinforced compound with respect to steel and to plant coating after thermal ageing, for 100 days at Tmax + 20°C

23°C

≥0.04

Cohesive separation mode Coverage ≥ 95%

0.38

Cohesive separation mode Coverage ＞ 95%

95°C

≥0.02

0.04

Adhesion test of reinforced compound with respect to steel and to plant coating after hot-water immersion, for 100 days at Tmax + 20°C

23°C

≥0.04

Cohesive separation mode Coverage ≥ 95%

0.35

Cohesive separation mode Coverage ＞95%

95°C

≥0.02

0.025

Adhesion test of compound without reinforcement with respect to steel and to plant coating before and after thermal ageing and before and after hot-water immersion, both for 100 days at Tmax + 20°C

23°C

-

The coating shall leave a film of compound on the substrate.

The coating leave a film of compound on the substrate.

13.5.9 (and M.3 and Annex I)

95°C

Lap shear resistance

23°C

N/mm²

≥0.004

Cohesive separation mode Coverage ≥95%

0.025

Cohesive separation mode Coverage ≥95%

Annex I

95°C

≥0.002

0.003

Specific electrical insulation resistance

RS100

23°C

Ω⋅m²

≥10⁸

≥0.8^a

1.0x10¹⁰

0.9

Annex F

RS100/RS70

-

Complete Coating

Impact resistance

23°C

J

≥15

＞15

Annex D

Indentation resistance

FJC Type

23°C and 95°C

N/mm²

13A

13A

Annex E

Test pressure

1.0

1.0

Residual thickness

mm

≥0.6

1.2

Cathodic disbondment resistance at 28 days

23°C and 95°C

mm

0 mm, no holiday

0 mm, no holiday

Annex G (and Annex C and 13.5.7)